TitleEvolution of crystalline aluminates from hybrid gel-derived precursors studied by XRD and multinuclear solid-state MAS NMR : I. Celsian, BaAl2Si2O8
Publication TypeJournal Article
Year of Publication1999
AuthorsMackenzie, K.J.D., and Kemmitt T.
JournalThermochimica Acta
Volume325
Issue1
Pagination5 - 12
Date Published1999
ISSN00406031 (ISSN)
AbstractHybrid gels of celsian composition were prepared from Al alkoxide, tetrathylorthosilicate (TEOS) and Ba acetate and their structure evolution was studied up to 1300°C by thermal analysis and X-ray diffraction. Information on their pre-crystallization behaviour was also provided by 27Al, 29Si and 137Ba MAS NMR spectroscopy. Apart from some excess Ba acetate which decomposed to traces of BaCO3 and BaO by ca. 500°C, the gels are X-ray amorphous and relatively homogeneous, and begin to crystallize to hexagonal celsian at 900°C. From ≈500°C onwards, an Al-substituted tetrahedral SiO4 framework begins to be established, evidenced by a progressive increase in the tetrahedral 27Al sites and the Q4(4Al) 29Si resonance. Migration of Ba into the polyhedral celsian sites occurs much more slowly. A small amount of mullite and Ba2SiO4 which crystallize from Al-rich and Ba-rich regions, respectively, also form crystalline celsian in secondary reactions at ca. 1100°C. The observation of a 27Al shoulder at ca. 36 ppm at 500-900°C may arise from Ba-poor mullite-like regions.
URLhttp://www.scopus.com/inward/record.url?eid=2-s2.0-0002394055&partnerID=40&md5=ef36b350e78e0fc86c923da100c844db

Back to top